多吡啶钴(Ⅲ)配合物与Zn~(2+)形成的新型“关-开”荧光探针
作者: 张黔玲, 刘剑洪, 任祥忠, 李翠华, 张培新, 刘建忠, 计亮年 主题: 多吡啶钴配合物, DNA, Zn~(2+), 荧光 年份: 2006
摘要: the formation of heterobimetallic complex [co(bpy)2(odhip)zn]5+ by [co(bpy)2odhip]3+ and zn2+ was investigated. the luminescent property of complex was also studied. the results indicated that the nonluminescent monometallic complex [co(bpy)2odhip]3+ could coordinated with zn2+ to form the luminescent heterobimetallic complex [co(bpy)2(odhip)zn]5+, the emission intensity increased as increasing the amounts of zn2+. the luminescence became the strongest at the ratio of czn / cco of 1. after binding to dna, [co(bpy)2odhip]3+ must change its binding mode from partial intercalation to intercalation to make the peripheral coordination site on the odhip ligand accessible for zn2+, the coordination occurred from the opposite side of helix with respect to the intercalated [co(bpy)2odhip]3+, and the luminescent heterobimetallic complex [co(bpy)2(odhip)zn]5+ was formed. on the other hand, [co(bpy)2(odhip)zn]5+ bound to dna by intercalation and situated the region of the intercalated [co(bpy)2odhip]3+ between the base p...
镁离子掺杂对磷酸铁锂结构和性能的影响
作者: 张培新, 文衍宣, 刘剑洪, 许启明, 任祥忠, 张黔玲 主题: 锂离子电池, 正极材料, LiFePO4, 镁掺杂 年份: 2006
摘要: 为提高lifepo4的充放电性能,用化学沉淀法制备了镁离子掺杂的磷酸铁锂,用电化学方法测量了li1-xmgxfepo4(x=0.00、0.02、0.05、0.07、0.10和0.20,摩尔分数)的充放电性能,用x射线衍射(xrd)和里特沃尔特(rietveld)方法表征了掺杂对lifepo4的晶体结构的影响。结果表明少量镁离子掺杂能有效地提高lifepo4的比容量和循环性能,其中li0.95mg0.05fepo4具有更好的电化学性能,放电比容量高出lifepo4约20mah/g,镁离子掺杂提高了lifepo4中fe3+/fe2+共存态的浓度,使材料具有更好的导电能力。
超声波化学法制备纳米铁酸锌粉末的影响因素
作者: 吕维忠, 刘波, 罗仲宽, 任祥忠, 蔡弘华, 张培新, 刘剑洪 主题: 铁酸锌, 纳米粒子, 超声波化学 年份: 2007
摘要: 超声辐射fe(no3)3.9h2o、不同锌盐和脲的混合水溶液得到前驱体,再经过高温焙烧得到纳米znfe2o4粉末。得到的纳米znfe2o4粉末用x射线衍射(xrd),傅立叶转换红外光谱(ft-ir)表征得到确认。系统研究了超声波化学法制备纳米铁酸锌粉末工艺中不同锌盐、超声波辐射时间、焙烧温度和焙烧时间等影响因素,结果表明:fe(no3)3.9h2o与zn(no3)2.6h2o为原料,超声波辐射为4h,焙烧温度为950℃,焙烧时间为14h可制备结晶良好、分散性好、粒度小于100nm的尖晶石型铁酸锌粉末。
蛋白质接枝共聚研究进展
作者: 宋艳, 刘剑洪, 张培新, 张黔玲, 任祥忠 主题: 接枝共聚, 酪蛋白, 丝素蛋白, 结构, 性能 年份: 2005
摘要: 接枝共聚是一种有效的化学修饰方法,经过接枝改性后,高分子化合物的物理、机械和化学性质都能得到改善。文章从引发体系、接枝单体两个方面综述了酪蛋白和丝素蛋白的接枝共聚改性机理以及接枝产物的结构和性能。接枝反应中引发剂浓度和接枝单体浓度都有一个最佳值,接枝产物的热性能和力学性能都有所提高。
纳米PbSnO_3的制备及其燃烧催化性能的研究
作者: 洪伟良, 刘剑洪, 田德余, 罗仲宽, 张培新, 魏波 主题: 纳米复合粒子, PbSnO3, 共沉淀法, 催化剂黑索今热分解 年份: 2004
摘要: nanocomposite pbsno3 was synthesized by coprecipitation method , and its phase evolution process was investigated. the particle size, crystal form, and phase of samples were determined with xrd, tem and eds. the catalytic actiyity of sample on the thermal decomposition of rdx was investigated by dsc. the results show that nanocomposite pbsno3 with the diameter of 9 nm can be obtained by calcining at 600 ℃ for 2 h, which crystal is cubic (pyrochlore type). the catalytic actiyity of nanocomposite pbsno3 on the thermal decomposition of rdx is much higher than that of normal pbsno3. the nanocomposite pbsno3 can decrease the peak temperature of thermal decomposition of rdx from 240.1 ℃ to 236.5 ℃, and the decomposition enthalpy δh of rdx increases 722 j·g-1 (about 70%).
以接枝酪蛋白与聚吡咯为复合载体的葡萄糖氧化酶电极的研究
作者: 任祥忠, 刘剑洪, 张黔玲, 张培新, 罗仲宽, 顾宜 主题: 接枝酪蛋白, 聚吡咯, 葡萄糖氧化酶, 复合载体 年份: 2005
摘要: 通过多步电化学聚合的方法,合成了以接枝酪蛋白与聚吡咯为复合载体的葡萄糖氧化酶电极,研究了工作电位、底物浓度、温度、溶液ph对电极电化学响应特性的影响,以及电极的灵敏性、专一性和重复性实验。实验结果表明:该酶电极的线性响应范围为1.0×10-6~1.43×10-2mol/l,其检出限为1.0×10-7mol/l,响应时间仅为8s,使用寿命超过1个月,并具有优良的重复性和高选择性。
超声-化学沉淀法制备纳米尖晶石型铝酸锌
作者: 刘波, 吕维忠, 罗仲宽, 任祥忠, 张培新, 刘剑洪 主题: 尖晶石型, 纳米颗粒, ZnAl2O4, 超声波化学, 制备, 表证 年份: 2008
摘要: 用超声-化学沉淀法制备了纳米铝酸锌(znal2o4)粉末。超声辐射al(no3)3.9h2o、zn(no3)2.6h2o和沉淀剂得到沉淀物,再在850℃烘5h制得平均粒径40nm的纳米znal2o4粉末。得到的纳米znal2o4粉末用x射线衍射(xrd),扫描电子显微镜(sem),傅立叶转换红外光谱(ft-ir)进行表征并得到确认。
超声波化学法制备纳米尖晶石型铁酸锰
作者: 吕维忠, 罗仲宽, 刘波, 张培新, 蔡弘华, 任祥忠, 刘剑洪 主题: 超声波化学, 纳米颗粒, 铁酸锰, 尖晶石型, 制备 年份: 2008
摘要: 在超声波辐射下,用前驱体法合成了纳米铁酸锰(mnfe2o4)粉末。超声辐射mncl2·4h20、fecl3·6h2o和脲得到前驱体,再在950℃烘15 h制得平均粒径约35 nm的纳米mnfe2o4粉末。得到的纳米mnfe2o4粉末用x射线衍射(xrd),透射电镜(tem),傅里叶转换红外光谱(ft-ir)进行表征并得到确认;产品磁学参数用样品振动磁强计进行了测定。
溶胶-凝胶法制备Li_2O-Al_2O_3-SiO_2微晶玻璃粉末
作者: 张培新, 许启明, 刘剑洪, 任祥忠, 罗仲宽, 张黔玲 主题: 溶胶-凝胶法, Li2O-Al2O3-SiO2, 微晶玻璃 年份: 2008
摘要: 采用溶胶-凝胶法制备了li2o-al2o3-sio2系玻璃粉末,利用x射线衍射(xrd)、红外光谱(ir)等手段研究了li2o-al2o3-sio2系玻璃的晶化过程,探讨了热处理温度和时间对晶相形成及晶体粒径的影响。结果表明:玻璃在热处理650℃下开始析晶,在1150℃左右晶体生长基本完全。随着热处理温度的升高和热处理时间的增加,晶体粒径增大。
CTAB/正己醇/水反胶束体系中合成PPy/TiO_2纳米复合粒子(英文)
作者: 任祥忠, 李溪, 刘剑洪, 梁讯, 张培新, 张黔玲, 罗仲宽, 顾宜 主题: 反胶束, 聚吡咯, 纳米复合粒子, TiO2 年份: 2008
摘要: 通过溶胶-凝胶法制备了tio2纳米粒子,并用十六烷基三甲基溴化铵(ctab)/正己醇/水反胶束体系作为微反应器合成了聚吡咯(ppy)/tio2纳米复合粒子。利用透射电镜(tem)、扫描电镜(sem)、红外光谱仪(ftir)、x-射线衍射仪(xrd)对纳米复合粒子进行了表征。实验结果表明,ppy/tio2球形粒子的平均粒径为150~200nm,在复合粒子中球形粒子占据优势,并有团聚的趋势。ftir和xrd结果显示纳米复合材料由ppy和tio2组成,无机复合粒子只有部分形成晶体。从该研究结果中可以看出,反胶束法可以有效地应用于有机-无机纳米复合材料的制备。